JUCOS Refractories > Shaped Refractories > Magnesia Chrome Brick
Product Details

Magnesia Chrome Brick are direct-bonded and made from high grade magnesite clinker and chrome oxide. By high pressure shaping and high temperature firing, its characteristic is the high direct-bonding rate, and big crystallite. It has a good thermal spalling resistance. The low–basic neutral nature gives itself a good slag resistance when servicing low–acid feed furnaces.

The fused-rebonded brick are made of fused mgo chrome clinker,its a realistic lining material for refining furnace, electric furnace, glass melting furnace,AOD COD RH etc.


Features Of Magnesia Chrome Brick

  • Good thermal shock resistance performance

  • Excellent resistance in slag abrasion

  • Good cold crush strength

  • Higher temperate resistant with good refractoriness

  • Higher grade of Chrome ore raw material

  • Lower impurity content

Applications Of Magnesia Chrome Brick

  • Rotary & Shaft Kiln


  • EAF & Ladle

  • Nonferrous Metal Furnace 

  • Hot-blast furnace

  • Glass kiln 

Specifications Of Magnesia Chrome Brick

  • Mgo and Cr2O3  content range from77% to 83%

  • Widely used throughout AOD COD RH EAF & Ladle Nonferrous Metal Furnace

Physical And Chemical Indicators For Magnesia Chrome Brick


RMC-22  RMC-16 RMC-12DMC-22 DMC-16 DMC-8
Apparent Porosity (%)151515161718
Bulk Density (g/cm3)
Cold Crushing Strength (MPa)505050404040
Thermal Linear Expansion(%)@ 1400℃1.81.5 1.2 1.81.5 1.2 

Thermal Shock Resistance air cool(times)605550404040

Refractoriness Under Load (℃) @0.2MPa170017001700170016501600

Composition (%)Cr2O322161222168

Main Applications     Rotary & Shaft Kiln
     EAF & Ladle 
     Nonferrous Metal Furnace                
     Hot-blast furnace
     Glass kiln